| Customization: | Available |
|---|---|
| Classification: | Magnesia-Chrome Brick |
| Refractoriness (℃): | 1580< Refractoriness< 1770, 1770< Refractoriness< 2000 |
|
Still deciding? Get samples of US$ 550/Ton
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Magnesia Chrome Brick are direct-bonded and made from high grade magnesite clinker and chrome oxide. By high pressure shaping and high temperature firing, its characteristic is the high direct-bonding rate, and big crystallite. It has a good thermal spalling resistance. The low-basic neutral nature gives itself a good slag resistance when servicing low-acid feed furnaces.
The fused-rebonded brick are made of fused mgo chrome clinker,its a realistic lining material for refining furnace, electric furnace, glass melting furnace,AOD COD RH etc.
FeaturesOf Magnesia Chrome Brick
Applications Of Magnesia Chrome Brick
Specifications Of Magnesia Chrome Brick
Physical And Chemical Indicators Of Magnesia Chrome Brick
| Description | RMC-22 | RMC-16 | RMC-12 | DMC-22 | DMC-16 | DMC-8 | |
| Bulk density (g/cm3) | 3.25 | 3.2 | 3.2 | 3.15 | 3 | 2.95 | |
| Cold Crushing Strength (MPa) | 50 | 50 | 50 | 40 | 40 | 40 | |
| Apparent Porosity(%) | 15 | 15 | 15 | 16 | 17 | 18 | |
| Thermal Shcok Resistamce 950ºC air cool(times) | 60 | 55 | 50 | 40 | 40 | 40 | |
| Thermal Linear expansion @1400ºC | 1.8 | 1.5 | 1.2 | 1.8 | 1.5 | 1.2 | |
| Refractoriness under Load (ºC)@0.2MPa | 1700 | 1700 | 1700 | 1700 | 1650 | 1600 | |
| Chemical Analysis (%) | MgO | 55 | 65 | 75 | 55 | 65 | 75 |
| Cr2O3 | 22 | 16 | 12 | 22 | 16 | 8 | |
| SiO2 | 1.5 | 1.5 | 1.5 | 2.0 | 2.0 | 2.5 | |
JUCOS providing high grade refractory brick and insulation thermal ceramic fiber products to globe industrial